    COEXISTENCE OF SUPERPARAMAGNETIC AND FERROMAGNETIC COMPONENTS IN (CuGa) 1-x Fe x Se 2-x SOLID SOLUTIONS WITH x=0.1, 1/3 and 1/2 ( COEXISTENCIA DE COMPONENTES FERROMAGNÉTICA Y SUPERPARAMAGNÉTICA EN SOLUCIONES SÓLIDAS (CUGA) 1-X FE X SE 2-X CON X=0.1, 1/3 Y 1/2 )
    (2018) P. Grima; Luis Nieves; Miguel Angel Alfaro Soto; Miguel Quintero; Humberto Cabrera; Inti Zumeta‐Dubé; Alejandro Rodríguez; Jennifer A. Aitken; P. Raics
    The magnetic behavior of (CuGa) 1-x Fe x Se 2-x solid solutions with compositions x=0.1, 1/3 and 1/2 has been investigated using SQUID techniques. DC magnetic susceptibility was measured in the temperature range 2 < T < 300K using Zero Field Cooling (ZFC) – Field Cooling (FC) protocol. It has been observed that the experimental curves can be analyzed as the sum of two magnetic components, one superparamagnetic and the other one ferromagnetic. The ferromagnetic component persist up to temperatures higher than room temperature making this report the first observation of room temperature ferromagnetism in A I B III C VI 2 compounds doped (or alloyed)with transition metals. El comportamiento magnetico de las soluciones solidas (CuGa) 1-x Fe x Se 2-x con composiciones x=0.1, 1/3 y 1/2 fue investigado por medio de la tecnica de SQUID. Las susceptibilidades DC fueron medidas en el rango de temperatura 2 < T < 300K usando el protocolo Enfriamiento a Campo Zero (ECZ) – Enfriamiento con Campo (EC). Se observo que las curvas experimentales podian ser analizadas como la suma de dos componentes magneticas, una superparamagnetica y otra ferromagnetica. La componente ferromagnetica persiste a temperaturas por arriba de la temperatura ambiente siendo este reporte la primera observacion de ferromagnetismo a temperatura ambiente en compuestos A I B III C VI 2 dopados (o aleados) con metales de transicion.
  • Thumbnail Image
    Item type: Item ,
    SYNTHESIS, CRYSTAL STRUCTURE AND MAGNETIC BEHAVIOR OF CuCo 2 InTe 4 AND CuNi 2 InTe 4 ( SÍNTESIS, ESTRUCTURA CRISTALINA Y COMPORTAMIENTO MAGNÉTICO DE CuCo 2 InTe 4 Y CuNi 2 InTe 4 )
    (2016) P. Grima; Miguel Angel Alfaro Soto; Orlando Izarra; Luis Nieves; Miguel Quintero; Gerzón E. Delgado; Humberto Cabrera; Inti Zumeta‐Dubé; Alejandro Rodríguez; Jennifer R. Glenn
    Polycrystalline samples of nominal CuCo 2 InTe 4 and CuNi 2 InTe 4 were prepared by the melt and anneal method and the products characterized by powder X-ray diffraction and SQUID techniques. It was found that CuCo 2 InTe 4 and CuNi 2 InTe 4 crystallize in the tetragonal space group (No 121), Z = 2, in a stannite-type structure, with the binaries CoTe and NiTe as secondary phases, respectively. The magnetic behavior of CuCo 2 InTe 4 is that of a superparamagnetic state with an irreversibility temperature of ~450K and a maximum coercive field of 35 Oe at 2K; whereas CuNi 2 InTe 4 shows two magnetic components, one diamagnetic an another weak ferromagnetic. Se prepararon muestras policristalinas de CuCo 2 InTe 4 and CuNi 2 InTe 4 en su valor nominal por el metodo de fusion y recocido, y los productos fueron caracterizados por las tecnicas de difraccion de rayos X y SQUID. Se encontro que CuCo 2 InTe 4 and CuNi 2 InTe 4 cristalizan en una estructura tetragonal, grupo espacial (No 121), Z = 2, tipo estannita, con presencia de los binarios CoTe y NiTe como fases secundarias, respectivamente. El comportamiento magnetico de CuCo 2 InTe 4 es de tipo superparamagnetico con una temperatura de irreversibilidad de ~450K y un campo coercitivo maximo de 35 Oe a 2K; mientras que CuNi 2 InTe 4 presenta dos componentes magneticas, una diamagnetica y otra ferromagnetica debil.