Carlos BloemM.D. SalvadorV. AmigóD. Busquets2026-03-222026-03-22200410.1533/wint.2004.3287https://doi.org/10.1533/wint.2004.3287https://andeanlibrary.org/handle/123456789/56619Citaciones: 1(2004). Microstructural change of the HAZ in an MIG welded bond on an AA7020 aluminium alloy: stress corrosion crack growth rate in dissimilar metal welds. Welding International: Vol. 18, No. 7, pp. 538-542.enMaterials scienceMetallurgyWeldingAluminiumAlloyCorrosionStress (linguistics)Aluminium alloyMetalGas metal arc weldingMicrostructural change of the HAZ in an MIG welded bond on an AA7020 aluminium alloy: stress corrosion crack growth rate in dissimilar metal weldsarticle