Andrade-Tacca, César A.Patiño Patiño, Ragihyth L.Urday Urday, Edwin2026-03-232026-03-2320220250-546010.34098/2078-3949.39.4.3https://doi.org/10.34098/2078-3949.39.4.3https://andeanlibrary.org/handle/123456789/96401Vol. 39, No. 4En las pilas alcalinas de Zn/MnO2, el dióxido de manganeso electrolítico (DME) se utiliza como cátodo y constituye una parte muy importante de los residuos domésticos que aportan metales pesados a los residuos sólidos urbanos. Este estudio describe la recuperación de DME por electro-oxidación en tela de carbón en licores ácidos lixiviados de baterías alcalinas usadas. Los rendimientos máximos de extracción para Mn y Zn fueron 43,68% (0,744 molL-1) y 56,11% (0,7321 molL-1) respectivamente. Los voltamogramas de un electrodo de carbón vítreo para la deposición de DME a partir de licores lixiviados se obtuvieron entre 0,0 y 1,4 V frente a ECS, y presentan un pico anódico a 1,2 V frente a ECS. Además, aparece un pico catódico a 0,97 V frente a ECS. La difracción de rayos X revela la presencia de nsutita (γ-MnO2) y manganita (γ-MnOOH) para todos los depósitos, y la morfología de los depósitos fue observada por microscopia electrónica de barrido (SEM).Electrodeposition of electrolytic manganese dioxide on carbon substrates from leachates from exhausted alkaline batteries . In the alkaline batteries of Zn/MnO2, the electrolytic manganese dioxide (EMD) is used as cathode and constitutes a very important part of household waste which contributes with heavy metals to the solid urban waste. This study describes the recovery of EMD by electro-oxidation on carbon cloth in acidic leached liquors from used alkaline batteries. The maximum extraction yield for Mn and Zn were 43.68% (0.744 molL-1) and 56.11% (0.7321 molL-1) respectively. The voltammograms of a vitreous carbon electrode for EMD deposition from leached liquors were obtained between 0.0 and 1.4V vs ECS, and exhibit an anodic peak at 1.2V vs ECS. In addition, a cathodic peak appears at 0.97V vs ECS. The x-ray diffraction reveals the presence of nsutite (γ-MnO2) and manganite (γ - MnOOH) for all deposits, and the morphology of the deposits was observed by SEM.esAlkaline batteriesManganese dioxideLeachingCarbon clothCarbon feltPilas alcalinasDióxido de manganesoLixiviaciónTelas de carbónFieltros de carbónArtículo Científico Publicado